Water-base Microlayer Corrosion Protection Coating JH-9390
- Location: CHINA
- FOB Price: ( Negotiable )
- Minimum Order Quantity: 40 Kilogram
- Packaging Detail: Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel
- Delivery Time: Ten days after receipt of advance payment Day
- Supplying Ability: 2 Ton / Day
- Payment Type: Other, L/C, T/T
Product Description
Product Details:
Brand Name: JUNHE
Model Number: JH-9390
Minimum Order Quantity: 100 Kilograms
Packaging Details: Pack A:16kg/ Metal Barrel
Pack B:24KG Plastic Barrel
Pack C:Based on the amount of B agent A
Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day
Coating Method: Dip Spin & Spray
PH: 3.8-5.2
Viscosity: 20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
Color: Silver
Specific Gravity: 1.30±0.05
Operating Temperature: 20±2℃
JH-9390 is made up of three packs: A, B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is 60~100.
Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the Cr6+.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
Coating Process:
1. Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )
2. Mixture Method
Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer , after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
Add B to the stirring A slowly. At the moment, the barrel temperature will go up, when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.
3. Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.
4. The coating should be filtrated by 80~100 mesh stainless steel screen before pouring into dip barrel.
5. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.
(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
6. Test density, PH, Temperature, Viscosity and Cr6+ content of coating every 8 hours if operate continuously.
Technical data:
Brand Name: JUNHE
Model Number: JH-9390
Minimum Order Quantity: 100 Kilograms
Packaging Details: Pack A:16kg/ Metal Barrel
Pack B:24KG Plastic Barrel
Pack C:Based on the amount of B agent A
Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day
Coating Method: Dip Spin & Spray
PH: 3.8-5.2
Viscosity: 20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
Color: Silver
Specific Gravity: 1.30±0.05
Operating Temperature: 20±2℃
JH-9390 is made up of three packs: A, B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is 60~100.
Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the Cr6+.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
Coating Process:
1. Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )
2. Mixture Method
Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer , after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
Add B to the stirring A slowly. At the moment, the barrel temperature will go up, when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.
3. Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.
4. The coating should be filtrated by 80~100 mesh stainless steel screen before pouring into dip barrel.
5. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.
(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
6. Test density, PH, Temperature, Viscosity and Cr6+ content of coating every 8 hours if operate continuously.
Technical data:
No. | Item | Data |
1 | Color | Silver |
2 | Coating method | Diping & Spraying |
3 | PH | 3.8-5.2 |
4 | Specific gravity | 1.30±0.05 |
5 | Viscosity | 20~60s(Spray Coating) 60~90S(Dip-Spin Coating) |
6 | Operating temperature | 20±2℃ |
Contact Information
- Company: Changzhou Junhe Technology Stock., LTD
- Address: Changzhou, Jiangsu, China
- Telephone: 86-051985911787
- Mobile: 018661228106
Company Profile
- Changzhou Junhe Technology Stock., LTD
- [ China ]
-
Changzhou Junhe Technology Stock.,ltd research and development center is located in changzhou national hi-tech zone, owns 15 acres of land for construction and is built around five categories of chemicals and equipment research and development and incubation bases, equipped with standardization on the basis of the experimental equipment and testing equipment of the company's marketing center an...
Basic Information
- Business Type: Manufacturing
- Company Products / Services: zinc flake coating, dip spin coating machine, dacromet coating, dip spin centrifugal coating machines, metal coating, junhe chemical
- Year Established: 1998
- Number of Employees: 101-500
- Website: http://www.junhete.com